AISI 1050 SAE UNS G10500
Carbon Steel Foundry
Steel foundry in China for producing
AISI 1050 SAE UNS G10500 Carbon Steel castings. The followings are
this material's chemical composition, physical and mechanical
properties and equivalent material grades.
The following
datasheet will give an overview of AISI 1050 carbon steel in detail.
Chemical
Composition
The chemical
composition of AISI 1050 carbon steel is tabulated below.
|
Element |
Content
(%) |
|
Iron,
Fe |
98.46-98.92 |
|
Manganese, Mn |
0.60-0.90 |
|
Carbon,
C |
0.470-0.55 |
|
Sulfur,
S |
≤ 0.050 |
|
Phosphorous, P |
≤ 0.040 |
Physical
Properties
The following
table shows the physical properties of AISI 1050 carbon steel.
|
Properties |
Metric |
Imperial |
|
Density |
7.85
g/cm3 |
0.284
lb/in³ |
Mechanical
Properties
The mechanical
properties of the cold drawn AISI 1050 carbon steel are outlined in
the following table.
|
Properties |
Metric |
Imperial |
|
Tensile
strength |
690 MPa |
100000
psi |
|
Yield
strength |
580 MPa |
84100
psi |
|
Shear
modulus (typical for steel) |
80 GPa |
11600
ksi |
|
Bulk
modulus (typical for steel) |
140 GPa |
20300
ksi |
|
Elastic
modulus |
190-210
GPa |
27557-30458 ksi |
|
Poisson’s ratio |
0.27-0.30 |
0.27-0.30 |
|
Elongation at break (in 50 mm) |
10% |
10% |
|
Reduction of area |
30% |
30% |
|
Hardness, Rockwell C (converted from Brinell hardness. Value
below normal HRC range, for comparison purposes only) |
13 |
- |
|
Hardness, Brinell |
197 |
197 |
|
Hardness, Knoop (converted from Brinell hardness) |
219 |
219 |
|
Hardness, Rockwell B (converted from Brinell hardness) |
92 |
92 |
|
Hardness, Rockwell C (converted from Brinell hardness. Value
below normal HRC range, for comparison purposes only) |
13 |
13 |
|
Hardness, Vickers (converted from Brinell hardness) |
207 |
207 |
Thermal
Properties
The thermal
properties of AISI 1050 carbon steel are given in the following
table.
|
Properties |
Metric |
Imperial |
|
Thermal
conductivity (typical steel) |
49.8 W/mK |
346 BTU
in/hr.ft².°F |
Other
Designations
Other
designations that are equivalent to AISI 1050 carbon steel include:
AMS 5085
ASTM A29 (1050)
ASTM A510
(1050)
ASTM A513
ASTM A519
(1050)
ASTM A576
(1050)
ASTM A682
(1050)
ASTM A827
ASTM A830
QQ S700 (C1050)
SAE J1397
(1050)
SAE J403 (1050)
SAE J412 (1050)