AISI 1015 SAE UNS G10150 Carbon Steel Foundry

Steel foundry in China for producing AISI 1015 SAE UNS G10150 Carbon Steel castings. The followings are this material's chemical composition, physical and mechanical properties and equivalent material grades.

The following datasheet provides an overview of AISI 1015 carbon steel.

Chemical Composition

The chemical composition of AISI 1015 carbon steel is outlined in the following table.

Element

Content (%)

Iron, Fe

99.13-99.57

Carbon, C

0.13-0.18

Manganese, Mn

0.30-0.60

Sulfur, S

≤ 0.050

Phosphorous, P

≤ 0.040

Physical Properties

The following table shows the physical properties of AISI 1015 carbon steel.

Properties

Metric

Imperial

Density

7.87 g/cc

0.284 lb/in³

Mechanical Properties

The mechanical properties of the cold drawn AISI 1015 carbon steel are displayed in the following table.

Properties

Metric

Imperial

Tensile strength

385 MPa

55800 psi

Yield strength

325 MPa

47100 psi

Bulk modulus (typical for steel)

140 GPa

20300 ksi

Shear modulus (typical for steel)

80.0 GPa

11600 ksi

Elastic modulus

190-210 GPa

27557-30458 ksi

Poisson's ratio

0.27-0.30

0.27-0.30

Elongation at break (In 50 mm)

18.00%

18.00%

Reduction of area

40.00%

40.00%

Hardness, Brinell

111

111

Hardness, Knoop (converted from Brinell hardness)

129

129

Hardness, Rockwell B (converted from Brinell hardness)

64

64

Hardness, Vickers (converted from Brinell hardness)

115

115

Machinability (based on AISI 1212 steel as 100 machinability. The machinability of Group I bar, rod, and wire products can be improved by cold drawing.)

60

60

Thermal Properties

The thermal properties of AISI 1015 carbon steel are given in the following table.

Properties

Metric

Imperial

Thermal expansion co-efficient (@0.000-100°C/32.0-212°F)

11.9 µm/m°C

6.61 µin/in°F

Thermal conductivity (estimated based on similar materials)

51.9 W/mK

360 BTU in/hr.ft².°F

Other Designations

Equivalent materials to AISI 1015 carbon steel are listed in the following table.

AMS 5060

ASTM A29

ASTM A510

ASTM A512 (1015, MT 1015)

ASTM A830

ASTM A519 (1015, MT 1015)

ASTM A545

ASTM A549 (1015)

ASTM A575 (M1015)

ASTM A576

ASTM A635

ASTM A659 (1015)

ASTM A787 (MT 1015)

ASTM A794

ASTM A513 (MT 1015)

SAE J1397

SAE J403

SAE J412

SAE J414

ASTM A108

FED QQ-S-698 (C1015)

MIL SPEC MJL-S-16974

 

 

 

Applications

AISI 1015 carbon steel can be used in forged, cold-headed or cold-formed parts which are low strength with wear resistant and hard surfaces.

 

Home | More Articles

 
  Gray Iron Castings  |  Ductile Iron Castings  |  Cast Steel Castings  |  Green Sand Iron Castings  |  Furan Resin Sand Castings  |  Automatic Molding Castings  |  Shell Molding Iron Castings  |  Sand Mold Steel Castings  |  Lost Wax Investment Castings  |  Stove & Boiler Metal Parts  |  Construction Machinery Parts  |  Agricultural Machinery Parts  |  Pump & Valve Metal Parts  |  Pipe Fittings & Manholes  |  Seeding Knife Points  |  Other Iron & Steel Castings  |  Prices Per Pound, Kg and Ton  |  Cast Iron Price Calculator  |
Cast Steel Price Calculator 
 

     © DANDONG FUDING ENGINEERING MACHINERY CO., LTD.  All Rights Reserved
     ADD: No.117, Zhenyang Street, Qianyang Town, Dandong City, Liaoning, P.R. China
     SITEMAP | China Foundry, China Turbocharger