AISI 1008 SAE UNS G10080 Carbon Steel Foundry

Steel foundry in China for producing AISI 1008 SAE UNS G10080 Carbon Steel castings. The followings are this material's chemical composition, physical and mechanical properties and equivalent material grades.

AISI 1008 carbon steel has excellent weldability, which includes projection, butt, spot and fusion, and brazeability. The following datasheet will provide more details about AISI 1008 carbon steel.

Chemical Composition

The following table shows the chemical composition of AISI 1008 carbon steel.

Element

Content (%)

Iron, Fe

99.31-99.7 %

Manganese, Mn

0.30-0.50 %

Carbon, C

0.10 %

Sulfur, S

0.050 %

Phosphorous, P

0.040 %

Physical Properties

The physical properties of AISI 1008 carbon steel are outlined in the following table.

Properties

Metric

Imperial

Density (composition 0.06% C, 0.38% Mn, 0.01% Si, annealed at 925°C)

7.872 g/cm3

0.2844 lb/in³

Mechanical Properties

The mechanical properties of cold drawn AISI 1008 carbon steel are tabulated below.

Properties

Metric

Imperial

Tensile strength

340 MPa

49300 psi

Yield strength (depending on temper)

285 MPa

41300 psi

Elastic modulus

190-210 Gpa

27557-30458 ksi

Bulk modulus (typical for steel)

200 GPa

29000 ksi

Shear modulus (typical for steel)

80.0 GPa

11600 ksi

Poisson’s ratio

0.27-0.30

0.27-0.30

Elongation at break (in 50 mm)

20%

20%

Reduction of area

45%

45%

Hardness, Brinell

95

95

Hardness, Knoop (converted from Brinell hardness)

113

113

Hardness, Rockwell B (converted from Brinell hardness)

55

55

Hardness, Vickers (converted from Brinell hardness)

98

98

Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing)

55

55

Thermal Properties

The thermal properties of AISI 1008 carbon steel are tabulated below.

Properties

Metric

Imperial

Thermal expansion co-efficient (@0.000-100°C/32-212°F)

12.6 µm/m°C

7 µin/in°F

Thermal conductivity (composition of 0.06% C, 0.4% Mn; 0°C )

65.2 W/mK

452 BTU in/hr.ft².°F

Other Designations

Equivalent materials to AISI 1008 carbon steel are as follows.

AMS 5040F

AMS 5042F

AMS 5044D

AMS 5047Ac

AMS 5050F

AMS 5053C

ASTM A108

ASTM A29

ASTM A510

ASTM A519

ASTM A545

ASTM A549

ASTM A575

ASTM A576

SAE J403

FED QQ-S-698 (C1008)

MIL-S-11310 (CS1008)

FED QQ-S-637 (C1008)

UNI CB 10 FU

SAE J1397

SAE J412

SAE J414

ASTM A512

ASTM A513

ASTM A575

ASTM A576

ASTM A635

ASTM A830

DIN 1.0204

 

 

 

 

 

 

Applications

AISI 1008 carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.

 

Home | More Articles

 
  Gray Iron Castings  |  Ductile Iron Castings  |  Cast Steel Castings  |  Green Sand Iron Castings  |  Furan Resin Sand Castings  |  Automatic Molding Castings  |  Shell Molding Iron Castings  |  Sand Mold Steel Castings  |  Lost Wax Investment Castings  |  Stove & Boiler Metal Parts  |  Construction Machinery Parts  |  Agricultural Machinery Parts  |  Pump & Valve Metal Parts  |  Pipe Fittings & Manholes  |  Seeding Knife Points  |  Other Iron & Steel Castings  |  Prices Per Pound, Kg and Ton  |  Cast Iron Price Calculator  |
Cast Steel Price Calculator 
 

     © DANDONG FUDING ENGINEERING MACHINERY CO., LTD.  All Rights Reserved
     ADD: No.117, Zhenyang Street, Qianyang Town, Dandong City, Liaoning, P.R. China
     SITEMAP | China Foundry, China Turbocharger