AISI 1006 SAE UNS G10060 Carbon Steel Foundry

Steel foundry in China for producing AISI 1006 SAE UNS G10060 Carbon Steel castings. The followings are this material's chemical composition, physical and mechanical properties and equivalent material grades.

The features of AISI 1006 carbon steel are mainly softness and ductility. The following datasheet will provide more details about AISI 1006 carbon steel.

Chemical Composition

The following table shows the chemical composition of AISI 1006 carbon steel.

Element

Content (%)

Iron, Fe

99.43-99.75

Manganese, Mn

0.25-0.40

Carbon, C

0.080

Sulfur, S

0.050

Phosphorous, P

0.040

Physical Properties

The physical properties of AISI 1006 carbon steel are outlined in the following table.

Properties

Metric

Imperial

Density

7.872 g/cm3

0.2844 lb/in³

Mechanical Properties

The mechanical properties of AISI 1006 cold drawn carbon steel are tabulated below.

Properties

Metric

Imperial

Tensile strength

330 MPa

47900 psi

Yield strength (depending on temper)

285 MPa

41300 psi

Elastic modulus

190-210 GPa

27557-30458 ksi

Bulk modulus (typical for steel)

140 GPa

20300 ksi

Shear modulus (typical for steel)

80.0 GPa

11600 ksi

Poisson’s ratio

0.27-0.30

0.27-0.30

Elongation at break (in 50 mm)

20%

20%

Reduction of area

45%

45%

Hardness, Brinell

95

95

Hardness, Knoop (converted from Brinell hardness)

113

113

Hardness, Rockwell B (converted from Brinell hardness)

55

55

Hardness, Vickers (converted from Brinell hardness)

98

98

Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing)

50

50

Thermal Properties

The thermal properties of AISI 1006 carbon steel are tabulated below.

Properties

Metric

Imperial

Thermal expansion co-efficient (@0.000-100°C/32-212°F)

12.6 µm/m°C

7 µin/in°F

Other Designations

Equivalent materials to AISI 1006 carbon steel are:

AMS 5041

ASME 5041

ASTM A29

ASTM A510

ASTM A545

FED QQ-W-461

MIL SPEC MIL-S-11310 (CS1006)

SAE J403

SAE J412 (1005)

SAE J414

Applications

AISI 1006 carbon steel is primarily used in applications which require hard bending and welding such as panels for appliances or automobiles. AISI 1006 carbon steel can also be used in magnet core applications.

 

Home | More Articles

 
  Gray Iron Castings  |  Ductile Iron Castings  |  Cast Steel Castings  |  Green Sand Iron Castings  |  Furan Resin Sand Castings  |  Automatic Molding Castings  |  Shell Molding Iron Castings  |  Sand Mold Steel Castings  |  Lost Wax Investment Castings  |  Stove & Boiler Metal Parts  |  Construction Machinery Parts  |  Agricultural Machinery Parts  |  Pump & Valve Metal Parts  |  Pipe Fittings & Manholes  |  Seeding Knife Points  |  Other Iron & Steel Castings  |  Prices Per Pound, Kg and Ton  |  Cast Iron Price Calculator  |
Cast Steel Price Calculator 
 

     © DANDONG FUDING ENGINEERING MACHINERY CO., LTD.  All Rights Reserved
     ADD: No.117, Zhenyang Street, Qianyang Town, Dandong City, Liaoning, P.R. China
     SITEMAP | China Foundry, China Turbocharger